Hot Dip Galvanized Cable Tray Commercial Grade And Fire Resistance For Maximum Performance

Hot dip galvanized cable tray involves immersing rust removed steel components in a solution of molten zinc at a temperature of around 600 ℃. This process attaches a layer of zinc to the surface of the tray steel components. This is done to prevent corrosion and achieve a long-lasting result.

The thickness of the zinc layer needs to be not less than 65 μm for thin plates below 5 mm. For thick plates, it should be 86 μm or more. Galvanizing forms a strong, abrasive layer that provides resistance to environmental factors such as moisture and corrosive chemicals.

Hot-dip galvanized cable trays have been adopted by many industries as they offer an effective method of metal corrosion prevention. They are widely used in metal structural facilities, serving as cost-effective solutions to cable management challenges.

• Excellent corrosion resistance: After hot-dip galvanizing treatment, a uniform zinc layer is formed on the surface of the hot-dip galvanized cable tray. This helps to prevent the steel substrate from coming into contact with any corrosive solution and protects the steel substrate from corrosion. Even in humid and chemically corrosive environments, the tray can still maintain its structural integrity for a long time, making it suitable for use in harsh environments such as chemical plants and marine areas.
• Long service life: The surface coating of hot-dip galvanized cable trays has high oxidation resistance, and the zinc layer has strong adaptability to temperature changes. It can still maintain good durability in high temperature environments, effectively extending the service life of the trays. Usually, the service life of hot-dip galvanized cable trays can reach several decades, far exceeding untreated metal trays.